Fig. 2From: Wet anisotropic etching characteristics of Si{111} in NaOH-based solution for silicon bulk micromachiningDifferent shapes formed by < 110 > crystallographic directions at which {111} planes appear during wet anisotropic etching process such as hexagonal, rhombus, triangle, isosceles trapezoidBack to article page